4.Results and Discussion
Effect of Acid.The kind of acid used in the aqueous
phase had a significant effect on the phase composition
of the TiO2 product.The feedstock was prepared as
follows:3.4 mL of tetrabutyl titanate and 4.0 or 8.0 mL
acid (5.0Mor 10.0Mhydrochloric acid or nitric acid) were
mixed,and this mixture was then added dropwise into
the other mixture of Triton X-100/n-hexanol clohexane.
The concentrations of tetrabutyl titanate and acid were
kept at 0.25Mand in the range of 0.5-2.0 M,respectively.
The hydrothermal reaction was first performed at 120 °C
for 12 h.The XRD patterns of the products prepared in
different acids with different acidity are given in Figure
1,and TEM micrographs of some products are shown in
4.Results and Discussion
Effect of Acid.The kind of acid used in the aqueous
phase had a significant effect on the phase composition
of the TiO2 product.The feedstock was prepared as
follows:3.4 mL of tetrabutyl titanate and 4.0 or 8.0 mL
acid (5.0Mor 10.0Mhydrochloric acid or nitric acid) were
mixed,and this mixture was then added dropwise into
the other mixture of Triton X-100/n-hexanol clohexane.
The concentrations of tetrabutyl titanate and acid were
kept at 0.25Mand in the range of 0.5-2.0 M,respectively.
The hydrothermal reaction was first performed at 120 °C
for 12 h.The XRD patterns of the products prepared in
different acids with different acidity are given in Figure
1,and TEM micrographs of some products are shown in